PLA SILK - 3D Filament - 1.75mm 50g - Pink

Due to its exceptional appearance, Silk filament is the most popular for the manufacture of decorative pieces. When printing with Silk filament, the final piece has a shiny, satin finish, which is not only apparently aesthetic, but also makes the transition between layers almost imperceptible.

PLA SILK has been improved with added polymers that give the material its high level of light dispersion and reflection, to achieve the silky surface finish that defines this filament. Based on PLA as the main material, it maintains the properties and advantages of standard PLA (easy modeling, absence of warping and low shrinkage) and even surpasses it in some aspects since it has greater mechanical and thermal resistance than PLA.

Characteristics:

• Diameter of 1.75mm
• 50 gram
  

General printing parameters:

• Nozzle temperature (between 200ºC and 230ºC)
• Bed temperature (between 50ºC and 70ºC)
• Fan: ON (100) %
  
  

Physical properties:

• Density: 1.24 g/cm3
• Flow rate: 8 g/10 min (ISO 1133-A)
• Flow rate: 3 g/10 min (ISO 1133-A)
• Sterochemical purity: 96 (% L-isomer)
• Residual monomer: 0.3% (max)
• Humidity (Karl Fisher Coulometric): 400 (max) ppm
• Melting temperature: 155º C Tm (DSC)
• Crystal transition temperature: 55-60º C Tg (DSC)

Mechanical properties:

• Tensile modulus: 3500 MPa (ISO 527-1)
• Tensile strength: 45 MPa (ISO 527-1)
• Strain at performance: 5% (max) (ISO 527-1)
• Impact with Charpy notches 23º C: ≤5 kJ/m2 (ISO 179-1eA)